On the Road to Conductors of the Future

  • Author: Angewandte Chemie International Edition
  • Published Date: 14 September 2020
  • Source / Publisher: Angewandte Chemie International Edition/Wiley-VCH
  • Copyright: Wiley-VCH GmbH
thumbnail image: On the Road to Conductors of the Future


Superconductivity in Hydrogen Sulfide

Superconducting wires can transport electricity without loss. This would allow for a reduction in power use, costs, and greenhouse gasses. Unfortunately, extensive cooling stands in the way, because existing superconductors only lose their resistance at extremely low temperatures. Vasily S. Minkov, Max Planck Institute for Chemistry, Mainz, Germany, and colleagues have introduced new findings about hydrogen sulfide in the H3S form, and its deuterium analogue D3S, which become superconducting at the relatively high temperatures of −77 and −107 °C, respectively.


This is even true in comparison with the current front-runners, copper-containing ceramics with transition temperatures that start at about –135 °C. Despite extensive research into sulfur/hydrogen systems, many important questions remain. Most importantly, superconducting hydrogen sulfide was previously produced from "normal" hydrogen sulfide, H2S, which was converted into a metal-like state with a composition of H3S under pressures of about 150 GPa (1.5 million bar).


Such samples were inevitably contaminated by hydrogen-depleted impurities that can distort experimental results. To avoid this, the researchers produced stoichiometric H3S by heating elemental sulfur directly with an excess of hydrogen (H2) with a laser, under pressure. They also produced samples made with deuterium.




High Transition Temperature

The cause of the relatively high transition temperature of H3S is its hydrogen atoms, which resonate with an especially high frequency within the crystal lattice. Because deuterium atoms are heavier than hydrogen, they resonate more slowly, so lower transition temperatures were expected for D3S. The team used a variety of analytical methods to refine the phase diagrams for H3S and D3S in relation to pressure and temperature, and to shed additional light on their superconducting properties.


At 111 to 132 GPa and 400 to 700 °C, the syntheses produced nonmetallic, electrically isolating structures (Cccm phases) that do not become a metal when cooled or pressurized further. They contain H2 (or D2) units within the crystal structure, which suppress superconductivity. The desired superconducting structures, cubic Im-3m phases, were obtained by syntheses above 150 GPa at 1200 to 1700 °C. They are metallic and shiny with low electrical resistance. At 148 to 170 GPa, samples of Im-3m-H3S had transition temperatures around −77 °C. The D3S analogues had a transition temperature of about −107 °C at 157 GPa, which is significantly higher than expected.


Decrease of pressure reversibly leads to an abrupt reduction of the transition temperature and loss of metallic properties. This is caused by rhombohedral distortions in the crystal structure (R3m phase). Heating under pressure irreversibly transforms the R3m phase into the Cccm phase. R3m is clearly a metastable intermediate phase that only occurs during decomposition. In the future, the researchers hope to find other hydrogen-rich compounds that can be converted to metals without high pressures and become superconducting at room temperature.


 

 

Article Views: 524

Sign in Area

Please sign in below

Additional Sign In options

Please note that to comment on an article you must be registered and logged in.
Registration is for free, you may already be registered to receive, e.g., the newsletter. When you register on this website, please ensure you view our terms and conditions. All comments are subject to moderation.

Article Comments - To add a comment please sign in

If you would like to reuse any content, in print or online, from ChemistryViews.org, please contact us first for permission. more


CONNECT:

ChemistryViews.org on Facebook

ChemistryViews.org on Twitter ChemistryViews.org on YouTube ChemistryViews.org on LinkedIn Sign up for our free newsletter


Magazine of Chemistry Europe (16 European Chemical Societies)published by Wiley-VCH