Wood As Hard As Steel

  • Author: ChemistryViews.org
  • Published: 10 February 2018
  • Copyright: Wiley-VCH Verlag GmbH & Co. KGaA
  • Source / Publisher: Nature/Nature Publishing Group
thumbnail image: Wood As Hard As Steel

Jianwei Song, University of Maryland, College Park, USA, and colleagues have made wood ten times more stable and harder than before through a two-step process. The treated wood is three times as dense and so strong that it can hardly be damaged by cracks and scratches.

In the first step, the researchers dip the wood into a hot bath of NaOH and Na2SO3. This treatment removes part of the lignin and hemicellulose from the wood. This makes the wood more porous and less stiff. However, the cellulose fibers of the wood are not affected. In the second step, the wood is compressed perpendicular to the growth direction at 100 °C. Under this pressure, many voids in the wood structure collapse, leading to a unique microstructure. The completely collapsed cell walls lead to a drastically increased contact surface between adjacent cellulose strands in the cell walls and fiber layers, which are stabilized by numerous hydrogen bonds.

This simple process works on a wide variety of wood types. While untreated wood significantly swells and softens at high humidity, the compacted wood barely loses strength and stability even at 95 % relative humidity. If the surface of the wood was painted, the material was even completely immune to moisture.

According to the researchers, their material rivals many metals with its tear resistance, stability, and weight. This makes the treated wood a cost-effective, high-performance, and lightweight alternative to materials such as steel, which could be used in cars, airplanes, and buildings.


 

Article Views: 1389

Sign in Area

Please sign in below

Additional Sign In options

Please note that to comment on an article you must be registered and logged in.
Registration is for free, you may already be registered to receive, e.g., the newsletter. When you register on this website, please ensure you view our terms and conditions. All comments are subject to moderation.

Article Comments - To add a comment please sign in

Bookmark and Share

If you would like to reuse any content, in print or online, from ChemistryViews.org, please contact us first for permission. more


CONNECT:

ChemistryViews.org on Facebook

ChemistryViews.org on Twitter ChemistryViews.org on YouTube ChemistryViews.org on LinkedIn Sign up for our free newsletter


A product of ChemPubSoc Europe (16 European Chemical Societies)and Wiley-VCH